This study evaluated the influence of different light sources on the conversion of different composite resins by Differential Scanning Calorimetry (DSC). Initially was determined the standard of the devices emission of light, one halogen light curing unit (Optilux 500 - Demetron/Kerr) and three generations of LEDs (LEC-470 I - MMOptics, Radii Plus - SDI and Ultra-Lume LED 5 - ULTRADENT), as for the spectrum and intensity. To measure the inorganic fraction of the composites (Durafill® VS - Heraeus-Kulzer, Tetric® Ceram - Ivoclar/Vivadent, Filtek Supreme XT - 3MESPE and Aelite LS Packable - Bisco) and its thermal stability, 3 specimens of each composite in cylindrical format, with 3mm of diameter and 1mm of depth, were confectioned, in a stainless steel matrix, light-cured and immediately submitted to the Thermogravimetry (TG). To the Differential Scanning Calorimetry (DSC), technique used in this experiment to determine the conversion of resin composites, 48 specimens were confectioned, in the same ratios of the used ones in the Thermogravimetry (TG). After to be removed of the matrix, each specimen was weighed in an analytical scale (SHIMADZU LIBROR AEG-SM - SHIMADZU CORP.), sealed in an aluminum crucible and taken for analysis. The data had been submitted to the analysis of variance test (p=0.002%) and Tukey test (p<0.05%). The results had allowed concluding that the intensity and compatibility of the spectral profile emitted by the light sources with the profile of absorption of the photoinitiators in composed resins have direct influence in the conversion during the polymerization process.

Este estudo avaliou a influência de diferentes fontes fotoativadoras, na conversão de resinas compostas, por meio da Calorimetria Exploratória Diferencial (DSC). Inicialmente, determinou-se o padrão de emissão de luz dos aparelhos, um a base de luz halógena (Optilux 500 Demetron/Kerr) e três gerações de LEDs (LEC-470 I MMOptics, Radii Plus SDI e Ultra-Lume LED 5 ULTRADENT), quanto ao espectro e intensidade. Com o objetivo de determinar a proporção em massa da parte inorgânica das resinas compostas (Durafill VS Heraeus-Kulzer, Tetric Ceram Ivoclar/Vivadent, Filtek Supreme XT 3MESPE e Aelite LS Packable Bisco) e a sua estabilidade térmica, foram confeccionados, em uma matriz de aço inoxidável, 3 corpos de prova de cada resina composta em formato cilíndrico, com 3mm de diâmetro e 1mm de profundidade, que após fotoativados e removidos da matriz eram imediatamente submetidos à Termogravimetria (TG). Para a Calorimetria Exploratória Diferencial (DSC), técnica utilizada neste experimento para determinar a qualidade da conversão das resinas compostas, foram confeccionados 48 corpos de prova, nas mesmas proporções dos utilizados na TG. Na DSC, após serem removidos da matriz, cada corpo de prova foi pesado em uma balança analítica eletrônica (SHIMADZU LIBROR AEG-SM SHIMADZU CORP.), selado em um cadinho de alumínio e levado para análise. Os dados foram submetidos à análise estatística com teste de variância (p0,002%) e teste de Tukey…

Advisors/Committee Members: Marcos Dias Lanza, Rodrigo de Castro Albuquerque, Lincoln Dias Lanza, Rodrigo de Castro Albuquerque, Lincoln Dias Lanza, Maria Irene Yoshida.

▼ 

O objetivo deste estudo foi avaliar a influência de duas técnicas de ativação complementar, sobre a resina composta Filtek P-60®, comparando-a com a resina composta laboratorial Artglass, por meio de ensaios de resistência ao dobramento e microdureza Vickers. Os grupos experimentais do estudo foram os seguintes: Grupo I fotoativação convencional utilizando o aparelho fotoativador Optlight Plus®; Grupo II após a fotoativação convencional, seguiu-se a ativação complementar por calor seco em estufa, a 125±2°C, por 600 segundos; Grupo III - após a fotoativação convencional, seguiu-se a ativação complementar por luz em uma unidade laboratorial UniXS®, por 360 segundos; Grupo IV fotoativação em uma unidade laboratorial UniXS®, por 360 segundos. Os grupos I, II e III foram confeccionados com Filtek P-60®, e o grupo IV com Artglass. Os ensaios de resistência ao dobramento seguiram os critérios da norma ISO 4049: 1988, e os ensaios de microdureza Vickers seguiram os critérios da norma ASTM E-384: 1999. Após os procedimentos de fotoativação e ativação complementar os corpos-de-prova foram mantidos em água deionizada a 37±1°C por 24 horas, armazenados, protegidos de luz ambiente. Após a análise estatística dos resultados pode-se concluir que, em relação à resistência ao dobramento, a ativação complementar da resina composta Filtek P-60, no grupo II e no grupo III, proporcionou um aumento desta propriedade. Os valores de resistência ao dobramento da resina composta Filtek P-60, no grupo I, foram estatisticamente iguais aos valores da resistência ao dobramento do grupo IV. Em relação à microdureza Vickers, a ativação complementar no grupo II e no grupo III, também proporcionou um aumento desta propriedade. Os valores de microdureza Vickers no grupo I foram superiores aos valores de microdureza Vickers do grupo IV. Pelo presente estudo pode-se sugerir a utilização da resina composta Filtek P-60® pela técnica indireta, submetida à ativação complementar por calor seco com propriedades de resistência ao dobramento e microdureza Vickers adequadas. Entretanto é importante salientar a necessidade da realização de outros testes laboratoriais, além de estudos de avaliação clínica, para que esta nova técnica possa ser indicada.

The purpose of this study was to assess the influence of two additional activation techniques on the composite resin Filtek P-60®, comparing it with the laboratorial composite resin Artglass, by means of bending strength and Vickers microhardness tests. The study experimental groups were the following: Group I conventional photoactivation using the photoactivator Optlight Plus®; Group II following the conventional photoactivation, the additional activation in a dry heat oven, at 125±2°C, for 600 seconds was carried out; Group III - after conventional photoactivation, the additional light activation in a laboratorial unit UniXS® for 360 seconds was carried out; Group IV photoactivation in a laboratorial unit UniXS®, for 360 seconds. Groups I, II and III were prepared with Filtek P-60®, and group IV with Artglass.…

Advisors/Committee Members: Joao Mauricio L de Figueiredo Mota, Joao Mauricio L de Figueiredo Mota, wagner reis da costa campos, Wagner Reis Campos, Gelson Luis Adabo, Claudia Silami de Magalhaes.

▼ 

O objetivo deste estudo foi avaliar a influência de duas técnicas de ativação complementar, sobre a resina composta Filtek P-60®, comparando-a com a resina composta laboratorial Artglass, por meio de ensaios de resistência ao dobramento e microdureza Vickers. Os grupos experimentais do estudo foram os seguintes: Grupo I fotoativação convencional utilizando o aparelho fotoativador Optlight Plus®; Grupo II após a fotoativação convencional, seguiu-se a ativação complementar por calor seco em estufa, a 125±2°C, por 600 segundos; Grupo III - após a fotoativação convencional, seguiu-se a ativação complementar por luz em uma unidade laboratorial UniXS®, por 360 segundos; Grupo IV fotoativação em uma unidade laboratorial UniXS®, por 360 segundos. Os grupos I, II e III foram confeccionados com Filtek P-60®, e o grupo IV com Artglass. Os ensaios de resistência ao dobramento seguiram os critérios da norma ISO 4049: 1988, e os ensaios de microdureza Vickers seguiram os critérios da norma ASTM E-384: 1999. Após os procedimentos de fotoativação e ativação complementar os corpos-de-prova foram mantidos em água deionizada a 37±1°C por 24 horas, armazenados, protegidos de luz ambiente. Após a análise estatística dos resultados pode-se concluir que, em relação à resistência ao dobramento, a ativação complementar da resina composta Filtek P-60, no grupo II e no grupo III, proporcionou um aumento desta propriedade. Os valores de resistência ao dobramento da resina composta Filtek P-60, no grupo I, foram estatisticamente iguais aos valores da resistência ao dobramento do grupo IV. Em relação à microdureza Vickers, a ativação complementar no grupo II e no grupo III, também proporcionou um aumento desta propriedade. Os valores de microdureza Vickers no grupo I foram superiores aos valores de microdureza Vickers do grupo IV. Pelo presente estudo pode-se sugerir a utilização da resina composta Filtek P-60® pela técnica indireta, submetida à ativação complementar por calor seco com propriedades de resistência ao dobramento e microdureza Vickers adequadas. Entretanto é importante salientar a necessidade da realização de outros testes laboratoriais, além de estudos de avaliação clínica, para que esta nova técnica possa ser indicada.

The purpose of this study was to assess the influence of two additional activation techniques on the composite resin Filtek P-60®, comparing it with the laboratorial composite resin Artglass, by means of bending strength and Vickers microhardness tests. The study experimental groups were the following: Group I conventional photoactivation using the photoactivator Optlight Plus®; Group II following the conventional photoactivation, the additional activation in a dry heat oven, at 125±2°C, for 600 seconds was carried out; Group III - after conventional photoactivation, the additional light activation in a laboratorial unit UniXS® for 360 seconds was carried out; Group IV photoactivation in a laboratorial unit UniXS®, for 360 seconds. Groups I, II and III were prepared with Filtek P-60®, and group IV with Artglass.…

Advisors/Committee Members: Joao Mauricio L de Figueiredo Mota, Wagner Reis da Costa Campos, Joao Mauricio L de Figueiredo Mota, Wagner Reis da Costa Campos, Gelson Luis Adabo, Claudia Silami de Magalhaes.

▼ 

Este estudo se propôs a 1) determinar o padrão de emissão de luz de dois aparelhos fotopolimerizadores, um convencional (HAL) e um LED; 2) comparar a emissão de luz do aparelho LED utilizando duas pontas condutoras distintas, a ponta acrílica disponibilizada pelo fabricante (LED A) e uma ponta de fibra óptica adaptada do aparelho convencional (LED F) e 3) avaliar a influência do padrão de emissão de luz destes aparelhos na quantidade de monômero não reagido de uma resina composta, através da calorimetria diferencial a varredura (DSC). Determinou-se o espectro de emissão e a potência de cada aparelho. A seguir, espécimes de resina composta (Charisma) foram fotopolimerizadas por 20 e 40s, em incremento único. Cada corpo de prova proporcionou três amostras representando cada um dos 3mm de sua profundidade. As amostras foram imediatamente submetidas à medida pela DSC. Os resultados obtidos mostraram que os LEDs apresentam uma densidade de potência menor que o aparelho convencional, mas o espectro de emissão destes aparelhos é semelhante ao espectro de absorção da canforoquinona. A mudança na ponta do aparelho LED melhorou a condução de luz e o LED F obteve resultados semelhantes ao aparelho convencional com 20s de exposição. O aumento do tempo de exposição não afetou os resultados para HAL e LED F e melhorou a polimerização para LED A, que necessitou de um tempo maior de exposição para conseguir a mesma conversão dos outros aparelhos. A eficácia de polimerização diminuiu com o aumento da profundidade, independente do aparelho avaliado.

The aim of this study was to compare the pattern of light emission of two light-curing units (a conventional Gnatus Optilight Digital/HAL and a LED Gnatus LED) and to evaluate the influence of this factor in the number of non-reacting monomers of a composite resin (Charisma) by differential scanning calorimetry (DSC). The LED was evaluated with two distinct light tips the acrylic tip of the commercial source (LED A) and an optical fiber tip which was adapted to the conventional device (LED F). Both the emission spectra and the power output of each source were then determined. Specimens of composite resin were photocured for 20 and 40s. Each specimen supplied three samples representing each one of the 3mm of its depth. The samples were then immediately subjected to measurement by DSC. The results obtained showed that the LEDs presented smaller irradiance than did the conventional source but the spectrum of emission of these light-curing units is similar to the absorption spectrum of canphoroquinone. The change in the LED tip improved the light conduction and the LED F obtained results similar to those of the conventional source at 20s exposure. The increase in exposure time didnt affect the results for HAL and LED F and improved the polymerization for LED A, which demanded a longer exposure time to achieve the same conversion of the others light-curing units. The effectiveness of polymerization decreased with the increase of depth, independent of the source evaluated.

Advisors/Committee Members: Luiz Thadeu de Abreu Poletto, Marcos Pinotti Barbosa, Lincoln Dias Lanza, Luiz Thadeu de Abreu Poletto, Glaura Goulart Silva.

▼ 

Objetivo: Este estudo investigou o desempenho clínico de restaurações Classes I e II de resina composta à base de dimetacrilato reparadas por uma resina composta de baixa contração à base de silorano e por uma resina composta à base de dimetacrilato, em baseline e ao longo de 6, 12 e 18 meses. Metodologia: Cem restaurações defeituosas de resina composta à base de dimetacrilato foram reparadas neste estudo. Destas, 93 foram examinadas uma semana após terem sido reparadas - baseline , 91 após 6 meses e 83 após 12 meses. As restaurações foram alocadas aleatoriamente em dois grupos de tratamento Controle (n=50): Adper SE Plus 3M /ESPE + Filtek P60 3M /ESPE e Teste(n=50): Sistema adesivo P90 3M /ESPE + Filtek P90 3M /ESPE. Dois examinadores devidamente calibrados (Kw = 0,78) fizeram a avaliação das restaurações reparadas de forma cega, independente e por meio de observação direta, tendo sido o estudo mascarado também para os pacientes. Os parâmetros clínicos analisados foram adaptação marginal, forma anatômica, rugosidade de superficíe, descoloração marginal, sensibilidade pós-operatória e cárie secundária, sendo as restaurações classificadas em Alfa, Bravo ou Charlie (critérios clínicos USPHS modificados). O teste de Mann-Whitney comparou os materiais testados, para todos os parâmetos clínicos, em baseline e após 6 e 12 meses ( = 0,05). O teste de Wilcoxon comparou os compósitos entre si em função do tempo baseline, 6 e 12 meses, para os mesmos parâmetros ( = 0,05). Resultados Preliminares: A perda de restaurações neste estudo foi de 9 % em 6 meses e de 17 % em 12 meses . Não houve diferença estatisticamente significativa entre as resinas Filtek P60 e Filtek P90 quando avaliados os parâmetros supracitados, em baseline, em 6 e 12 meses (p >0,05). Não houve diferença estatisticamente significativa entre os períodos de avaliação quando cada resina foi testada, considerando os mesmos parâmetros (p >0,05). Conclusões: Após um ano de avaliações, resinas compostas à base de silorano apresentaram um adequado desempenho clínico semelhante às resinas compostas à base de dimetacrilato quando utilizadas para reparar restaurações de resina composta à base de dimetacrilato. Quando bem planejados, os reparos podem ser um tratamento restaurador alternativo à substituição de restaurações com defeitos localizados, porém clinicamente aceitáveis, preservando estruturas dentais sadias, reduzindo custos e tempo clínico.

Purpose: To investigate clinical performance of defective conventional dimethacrylate-based composite resin restorations repaired by a low-shrinkage silorane-based composite or a dimethacrylate-based composite resin, at baseline, 6 and 12 months. Material and Methods: One hundred defective dimethacrylate-based composite resin restorations were repaired in this study. From those, 93 were examined at baseline, 91 at 6 months and 83 at 1 year. The restorations were randomly assigned to one of two treatment groups: Control (n = 50) Adper SE Plus, 3M /ESPE + Filtek P60 Posterior Restorative, 3M/ESPE and Test (n = 50) Repair with…

Advisors/Committee Members: Allyson Nogueira Moreira, Claudia Silami de Magalhaes, Allyson Nogueira Moreira, Claudia Silami de Magalhaes, Lia Silva de Castilho, Tulimar Pereira Machado Cornacchia, Raquel Conceição Ferreira, André Luís Faria e Silva.

▼ 

The aim of this study was to evaluate the marginal adaptation of two aesthetic restorative materials and to compare two techniques for ceramic construction. A standard class II cavity milled in stainless steel was made. The master model was molded with polyvinilsiloxane material and Noritake Super Dental Stone was poured. The indirect composite restorations were made by an increment of 0,2g adapted on the stone model cavity walls and activated for 180 seconds. An acrylic ring was adapted around the stone model and a second increment of 0,2g of indirect composite was adapted and another 180s activation cycle was applied. The acrylic ring was removed and another cycle of activation was made. The specimens were removed of the stone model and another 180activation cycle were applied whith the inner surface of the specimen pointed to the light. Tem specimens were made using DialogII., Vita-Zeta. and Solidex. indirect composite material. The ceramic specimens were made by duplication of stone models and pouring the refractory die material. Twenty refractory models were made. Ten stayed at room temperature and pressure during the set and ten were submitted in a 45psi positive pressure during the set. the ceramic restorations were constructed by the refractory die material technique. For the marginal evaluation, each restoration was seated in the master model with a 1,0Kgf vertical load by MP insertion gauge. All the specimens were measured ten times in an optical microscope Mitutoyo TM.. The mean of the results were submitted in ANOVA and Students t-test. There was no difference between ceramic or indirect composite restoration and there is no difference between the ceramic construction techniques.

O objetivo deste estudo foi avaliar a adaptação marginal de dois materiais restauradores estéticos e comparar a utilização de duas técnicas na confecção de restaurações cerâmicas. Foi utilizado para tanto, um troquel metálico simulando um preparo cavitário classe II composta. O troquel foi moldado com silicona de adição e o molde vazado com gesso-pedra tipo IV. As restaurações em resina composta indireta foram confeccionadas aplicando-se um primeiro incremento de resina composta indireta sobre o modelo de gesso e submetendo-o a um ciclo de ativação por luz. Um anel acrílico transparente foi adaptado em torno da região que simulou a caixa proximal e um segundo incremento foi aplicado, sendo ativado por mais um ciclo. O anel acrílico foi removido e mais um ciclo de ativação foi realizado. O corpo de prova foi removido do modelo de gesso e submetido a outro ciclo de ativação, com a superfície inferior voltada para a fonte de luz. Cada ciclo de ativação corrrespondeu a 180 segundos no aparelho de luz estroboscópica UniXS.. Foram confeccionados dez corpos-de-prova das resinas utilizadas, sendo estas Vita Zeta., DialogII. e Solidex.. Para a confecção das restaurações cerâmicas o modelo de gesso foi duplicado e o revestimento refratário foi vazado sobre a duplicação, tendo dez modelos sido submetidos à presa sob pressão positiva de…

Advisors/Committee Members: Joao Mauricio L de Figueiredo Mota, Joao Mauricio L de Figueiredo Mota, Mario Fernando de Goes, Ivan Doche Barreiros.

▼ 

Biocerâmicas associadas a polímeros para capeamento pulpar estão sendo investigadas pela capacidade de induzir a formação de tecido mineralizado. Esses materiais são usados na ortopedia e implantodontia com resultados clínicos eficientes. Contudo, pouco se sabe sobre seu efeito sobre a polpa dental e seus componentes celulares. O objetivo deste estudo foi avaliar a biocompatibilidade do compósito: biocerâmica de -tricálcio fosfato/hidroxiapatita (BC) e co- polímero ácido poli (lático-co-glicólico) (PLGA) (BC/PLGA), em cultura de fibroblastos da polpa dental humana (FP5) e de macrófagos peritoneais (MP), e avaliar a resposta pulpar após capeamento direto após 30 e 60 dias. A citotoxicidade foi avaliada através do ensaio MTT nos seguintes grupos: Controle (células), Compósito (BC/PLGA), BC e PLGA nos tempos de 0, 24 e 48h nos fibroblastos e 48h nos macrófagos. Ainda avaliou-se a aderência celular de fibroblastos gengivais humanos (FMM1) e MP sobre a superfície de discos de BC/PLGA. O resultado do ensaio MTT em FP5 foi analisado por ANOVA e Tukey. Houve crescimento celular progressivo dos FP5 em todos os grupos experimentais, semelhantes ao controle. Somente o grupo compósito apresentou diminuição da proliferação celular após 48 h em relação ao controle. Nos macrófagos não foi observado citotoxicidade em nenhum grupo (p>0,05). Excelente aderência celular dos FMM1 e dos MP foi observada por microscopia eletrônica de varredura (MEV) na superfície dos compósitos (>97 %). Para a avaliação da resposta pulpar e formação de ponte dentinária após capeamento direto foram estabelecidos os seguintes grupos: BC/PLGA, BC, PLGA, hidróxido de cálcio e controle negativo após 30 e 60 dias. No Grupo BC/PLGA, a avaliação histológica do estado pulpar geral mostrou vitalidade e inflamação predominantemente leve a moderada tanto no grupo de 30 e 60 dias, não apresentando diferença significativa entre eles (Exato de Fisher p>0,05). Na avaliação da formação de ponte dentinária, após capeamento direto com BC/PLGA, houve formação de tecido mineralizado, observado a partir do 14o dia, sendo mais evidente no 30o dia em 90% das amostras. Entretanto, após 60 dias os resultados mostraram presença de ponte dentinária em 60% e houve diferença significativa com o grupo de 30 dias (Person Chi-Square p<0,05). Em conclusão, o compósito BC/PLGA não interfere na proliferação de fibroblastos humanos, foi biocompatível com os macrófagos, permite a aderência celular sobre os discos. O compósito BC/PLGA teve excelente desempenho no capeamento pulpar direto após 30 dias no modelo experimental utilizado, contudo, após 60 dias houve diminuição na porcentagem da presença de ponte dentinária, por tanto, sugere-se a necessidade de testá-lo em outros modelos experimentais, in vivo.

The pulp capping with bioceramics, polymers and cements biomaterials able to trigger resident cells in the pulp to differentiate into odontoblast-like cells and to induce the formation of tertiary dentin is being investigated. The aim of the present study was to assess the cell viability…

Advisors/Committee Members: Maria Esperanza Cortes Segura, Ruben Dario Sinisterra Millan, Maria Esperanza Cortes Segura, Ruben Dario Sinisterra Millan, Márcia Martins Marques, Hercílio Matelli Júnior, Celia Regina Moreira Lanza, Patricia Valente Araujo Jacques Goncalves, Vagner Rodrigues Santos, Maria Aparecida Borsatti.

▼ 

Introdução: O uso de resinas compostas aquecidas já foi sugerido na literatura como um agente de cimentação para restaurações indiretas. Porém, ainda não existe nenhum relato da resistência de união destes materiais comparados com os agentes mais utilizados para este fim, os cimentos resinosos. Objetivo: Avaliar o efeito do aquecimento de resinas compostas utilizadas como agente de cimentação sobre a resistência de união e formação de interface adesiva em restaurações indiretas. Metodologia: Neste estudo in vitro foram utilizados 50 terceiros molares humanos extraídos, que foram preparados através de secção transversal da coroa dental para criar uma superfície plana de dentina. Para a confecção das restaurações foi utilizada uma matriz de PVC circular com altura de 2 e 4 mm que foi preenchida com resina composta fotopolimerizável (Tetric N’Ceram) e prensada entre duas fitas de poliéster para a polimerização. Foram formados então 10 grupos experimentais (n= 5) nos quais houve a variação do fator material (cimento resinoso RelyX, resina composta Venus e Z250 XT, aquecidas e não aquecidas) e do fator altura através das peças de duas diferentes espessuras (2 e 4 mm). Os procedimentos adesivos e de cimentação para todos os grupos experimentais foram realizado com os dentes sob pressão pulpar induzida. A variável de resposta resistência de união, em MPa (Mega Pascal), foi avaliada quantitativamente através de ensaios de microtração. A análise estatística foi realizada através do teste ANOVA e do teste de Tukey (α=0,05). Para a visualização da formação da camada híbrida, uma fatia de um dente de cada grupo experimental foi preparada e observada em Microscopia Eletrônica de Varredura (MEV) para o registro de microfotografias e análise qualitativa. Resultados: Houve diferença estatística entre os grupos testados. O calor não aumentou os valores de resistência de união das resinas compostas, com exceção do grupo da resina Venus sob peças de 4 mm. O aquecimento do material demonstrou diminuição da interface adesiva e interação mais íntima do agente com o adesivo nas microscopias. Conclusões: O pré-aquecimento da resina composta não influenciou na resistência de união, exceto para a resina Venus sob peças de 4 mm. O efeito da alteração de viscosidade dos materiais aquecidos pode ser notado na interface adesiva. Não houve diferença na resistência de união entre as restaurações de 2 e 4 mm de altura.

Introduction: The use of pre-heated composites has been already suggested as an agent for luting indirect restorations. However, there is still no report on the bond strength of those materials compared with resin cements, the agents most commonly used for this purpose. Objective: The aim of this in vitro study was to evaluate the effect of pre-heating resin composites used as a luting agent of indirect restorations on the bond strength and resin-dentin bonded interface. Methods: Fifty sound extracted third molars were selected. Each tooth had the occlusal surface removed to create a flat dentin surface. Indirect restorations were…

Advisors/Committee Members: Erhardt, Maria Carolina Guilherme.

▼ 

Este trabalho avaliou a influência das variáveis: tempo de exposição à luz (20, 30, 40 e 60s), intensidade da fonte halógena (180 e 580 mW.cm-2) e distância (0, 3, 6 e 8mm) entre a fonte de luz e resina odontológica nanoparticulada (Supreme – 3MESPE) sobre as propriedades e características finais da mesma. As propriedades avaliadas foram: microdureza, resistência à compressão, resistência à compressão diametral, força de contração por polimerização, estabilidade térmica, morfologia (fractografia) e interface cavidade-material restaurador. Os resultados significativos foram os seguintes: a) o aumento do tempo e intensidade de fotoativação produz aumento da microdureza em ambas as superfícies da amostra, enquanto o aumento da distância gera uma diminuição da microdureza; b) sobre a resistência à compressão e compressão diametral: o aumento do tempo e intensidade de irradiação aumenta a resistência à compressão, enquanto o aumento da distância faz com que diminua tal resistência; c) na contração por polimerização um aumento de intensidade de irradiação provocou um aumento na contração, não tendo o tempo e a distância efeitos sobre a mesma; d) sobre a estabilidade térmica: não houve diferenças significativas entre as resinas após polimerização. Todas elas apresentam, entretanto, maior estabilidade térmica do que a resina não polimerizada. e) morfologia da superfície de fratura (fractografia): os cones de fratura ocorreram perpendicularmente à força aplicada, sendo dependentes da intensidade e distância. f) interface cavidade/resina: a intensidade é principal fator gerador de desadaptações na interface cavitária.

This work has evaluated the influence of the experimental conditions like irradiation time, source power and distance between the light source and a nanoparticle composite resin (Supreme - 3MESPE), on the properties of the polymerized resin. Such properties are: microhardness, compression strength, diametral compression strength, contraction force induced by polymerization, thermal stability, morphology (fractography) and the interface properties between restorative material and cavity. The significant and conclusive results are the following: a) the increasing time and source power causes an increasing in both sample surfaces, while an increase in irradiation distance generate a decrease in microhardness; b) about the compressions strength and diametral compression strength: increasing time and source power, the compression strength increases, while an increase in the distance between tip an sample has an opposite effect; c) in the contraction induced by polymerization an increase in the source power causes a higher contraction. Time and distance has no effect in this property; d) with respect to the thermal stability there are no significant differences between the irradiated samples, but all them are more stable that the starting resin; e) surface fracture morphology: a standard conical profile takes place under drastic irradiation conditions, mainly on source power and distance; f) resin/cavity…

Advisors/Committee Members: Baumhardt Neto, Ricardo.

▼ 

Tensões geradas pela contração de polimerização das resinas compostas podem resultar em falha das restaurações devido a sensibilidade pós-operatória, margens imperfeitas e lesões secundárias de cárie. Uma resina composta com matriz de silorano foi recentemente comercializada, tendo como principal característica a reduzida contração de polimerização. Este estudo clínico tipo split-mouth comparou o desempenho da resina composta FiltekTM P90 / P90 Adhesive System (3M-ESPE) com o da resina composta FiltekTM P60 / Adper TM SE Plus (3M-ESPE), em restaurações de classe I oclusais. Cada indivíduo (n=35) recebeu pelo menos um par de restaurações, alocadas aleatoriamente em grupo teste (P90) e grupo controle (P60). Um único operador realizou os preparos e restaurações, usando os materiais segundo orientações do fabricante. Após uma semana, as restaurações receberam acabamento e polimento e foram avaliadas de forma cega e independente por dois examinadores treinados (kW 0,7). Após 3 meses, as restaurações foram reavaliadas pelos mesmos examinadores (KW = 0,84). Foram utilizados os critérios United States Public Health Service modificados nas avaliações das restaurações. O teste de Wilcoxon comparou as frequências de escores Alfa, Bravo e Charlie nos grupos teste e controle no baseline e após 3 meses. Os resultados foram considerados significativos para uma probabilidade de significância inferior a 5%. No baseline e após 3 meses, não houve diferença estatística significativa entre os grupos quanto aos critérios de descoloração marginal, integridade marginal, textura de superfície, forma anatômica, sensibilidade pós-operatória e cárie secundária (p>0,05). Após 3 meses, não houve diferença significativa nos critérios avaliados dentro de cada grupo (p>0,05). Concluiu-se que, no período de avaliação inicial, o desempenho clínico da resina de silorano foi similar ao da resina de metacrilato.

Tensions generated by the polymerization shrinkage of composite resins can result in failure of restorations due to post-operative sensitivity, marginal gaps and secondary caries lesions. A silorane composite matrix was recently launched in the market, the main feature of the low polymerization shrinkage. This split-mouth clinical study compared the performance of composite resin FiltekTM P90 / P90 Adhesive System (3M-ESPE) with composite resin FiltekTM P60 / Adper TM SE Plus (3M-ESPE) in Class I occlusal restorations. Each individual (n = 35) received at least one pair of restorations, randomly allocated in the test group (P90) and control group (P60). A single operator carried out the preparations and restorations, using the materials in accordance with manufacturer s guidelines. A week later, the restorations were finished and polished and were evaluated blindly and independently by two trained examiners (kW 0.7). Three months after the restorations were evaluated again by the same two trained investigators blindly and independently (kW 0.84) using the modified United States Public Health Service criteria. Wilcoxon test compared the…

Advisors/Committee Members: Claudia Silami de Magalhaes, Allyson Nogueira Moreira, Claudia Silami de Magalhaes, Allyson Nogueira Moreira, Raquel Conceição Ferreira, Tulimar Pereira Machado Cornacchia, Joao Batista Novaes Junior, Rodrigo Richard da Silveira.

▼ 

A longevidade e durabilidade das restaurações cerâmicas cimentadas adesivamente dependem da qualidade e da estabilidade da união entre a superfície interna da cerâmica e o cimento resinoso. Os valores de resistência de união por microtração têm sido utilizados como preditivos do sucesso clínico destes trabalhos. Com o objetivo de avaliar a influência do tratamento térmico do silano sobre a resistência adesiva entre uma cerâmica e um cimento resinoso quimicamente ativado (C&BÔ), dezoito blocos de IPS Empress®2 foram confeccionados, planificados com lixas (granas 240 e 320) e cimentados a dezoito blocos de resina composta (InTen-S®) utilizando-se um sistema adesivo químico (Lok®). Definiram-se 6 grupos de 3 blocos, conforme o tipo de tratamento da superfície da cerâmica: G1) sem tratamento; G2) HF (Ácido Fluorídrico 10%) + S (silano Monobond-S® com microbrush, seco a temperatura ambiente 3min); G3) S + enxágüe em água corrente + temperatura ambiente (3min); G4) S + enxágüe com água em ebulição 5s + temperatura ambiente (3min); G5) S + enxágüe com água em ebulição 5s + secagem a 50ºC (3min); G6) silano seco a 50ºC (3min) + enxágüe com água em ebulição 5s + temperatura ambiente (3min). Os corpos-de-prova em forma de palito (CP) foram obtidos por corte dos blocos de cerâmica/resina 7 dias após a cimentação e submetidos à microtração (0,5mm/min) após 30 dias de armazenamento em água. Desenvolveu-se um dispositivo para a fixação dos CP pelas extremidades ao invés de pelas laterais. Todos os CP do G1 desuniram durante o corte. Os valores médios de tensão de ruptura em MPa (com desvio padrão) foram estatisticamente superiores para G2 (14,77±8,31) comparados aos de G4 (8,45±4,51) e G5 (9,46±5,26), estatisticamente semelhantes entre si e superiores a G3 (6,60±3,50) e G6 (5,94±4,27), estatisticamente semelhantes entre si. A fractografia por microscopia óptica (50x) demonstrou que todas as fraturas ocorreram dentro da zona de adesão e foram adesivas em 100% das amostras de G3 e G6. Observaram-se falhas coesivas em 24% das amostras em G4, 30% em G2 e em 40% das amostras de G5. Observou-se correlação entre a ocorrência de fraturas coesivas e maiores valores de resistência de união. Concluiu-se que a aplicação do Silano influenciou positivamente a resistência de união, em comparação com o controle negativo, mas sua efetividade foi maior quando sobreposto ao condicionamento com HF (G2).

Ceramic-bonded restoration longevity and durability are related with the quality and stability of the bond between the ceramic surface and the luting agent. Microtensile bond strength values have been used to predict the clinical success of these restorations. With the aim to evaluating the influence of silane heat treatment on the bond strength between a ceramic and a composite chemmically activated resin cement (C&BÔ), eighteen blocks of IPS Empress®2 were fabricated, flattened (240 320-grit metallographic paper) and luted to composite resin blocks (InTen-S®) using a chemical adhesive system (Lok®). Six groups with three blocks each were analyzed…

Advisors/Committee Members: Vicente Tadeu Lopes Buono, Joao Mauricio L de Figueiredo Mota, Vicente Tadeu Lopes Buono, Luiz Thadeu de Abreu Poletto, Ronaldo Antonio Neves M Barbosa, Joao Mauricio L de Figueiredo Mota.

▼ 

Tese de Mestrado, Medicina Dentária, Universidade de Lisboa, Faculdade de Medicina Dentária, 2014

Objetivo: Estudar a influência de três materiais de matriz oclusal na polimerização de um compósito, avaliando a capacidade de remoção da camada inibida, o efeito do oxigénio e do aumento do tempo de irradiação na polimerização, através de análise de microdureza. Métodos: Espécimes de compósito (Grandio®SO; VOCO) com 2 mm de espessura foram fotopolimerizados com um LED, com interposição do material em estudo [sem material, tira de acetato, Bite-Perf®(BITEPERF Dental Products), RegistradoClear (VOCO) e Memosil2 (Heraeus Kulzer)]. Fizeram-se três estudos (n=10). No estudo 1, avaliou-se a influência do aumento do tempo de polimerização, com e sem matriz interposta. No estudo 2, avaliou-se o papel do oxigénio na inibição da polimerização do compósito, preparando os espécimes numa atmosfera com azoto. No estudo 3, avaliou-se a capacidade de remoção da camada inibida, formada sob matriz de polivinilsiloxano, com acetona ou borracha. Efetuaram-se testes de microdureza Knoop no topo e base dos espécimes, 24 horas após a polimerização. Os resultados foram tratados estatisticamente com testes paramétricos MANOVA e SNK post-hoc com nível de significância de 5% e não paramétricos Kruskal-Wallis e Mann-Whitney. Resultados: No estudo 1, a microdureza dos grupos com matriz de Bite-Perf® aumentou com a polimerização adicional. Grupos com Memosil e RegistradoClear não apresentaram esse aumento. No estudo 2, só os grupos Memosil, RegistradoClear e Sem Acetato, em azoto, apresentaram microdureza no topo estatisticamente superior (p<0,05) à verificada em oxigénio. No estudo 3, a microdureza da superfície de topo nos grupos Memosil-Borracha, Memosil-Acetona, RegistradoClear-Borracha foi inferior à do grupo controlo com acetato. Conclusões: Com matriz de Bite-Perf® a fotopolimerização adicional permite aumentar a polimerização do compósito. O oxigénio inibe a polimerização do compósito quando se utilizam matrizes de polivinilsiloxano. A remoção da camada inibida com acetona e borracha leva a valores de microdureza no topo próximos dos valores da base.

Objective: To study the influence of three oclusal matrix materials on the polymerization of a resin composite, assessing the increasing irradiation time in polymerization, the effect of oxygen in the inhibited layer and the ability of removing the inhibited layer, through microhardness analysis. Methods: Composite specimens (Grandio®SO; VOCO), 2mm thick, were polymerized with a LED curing device, through the oclusal matrix materials [mylar strip, without mylar strip, Bite-Perf®(BITEPERF Dental Products), RegistradoClear (VOCO) and Memosil2 (Heraeus Kulzer)]. Three studies were made (n=10). In study 1, the influence of a longer irradiation period on the polymerization was evaluated. In study 2, the effect of oxygen in the creation of an inhibited layer was studied and so specimens were prepared in a nitrogen atmosphere. In study 3, the potential of acetone and rubber polishing techniques…

Advisors/Committee Members: Oliveira, Sofia Arantes e.

▼ 

Tese de mestrado, Medicina Dentária, Universidade de Lisboa, Faculdade de Medicina Dentária, 2016

As restaurações indiretas em resina composta foram introduzidas com o objectivo de ultrapassar as limitações das restaurações em resina composta pela técnica direta, que apesar da sua evolução relativamente à sua constituição e propriedades, apresentavam ainda limitações relativamente às suas propriedades mecânicas e contração de polimerização. A técnica indireta permite ainda o fabricação das mesmas em meio extra-oral, no laboratório através de enceramento, confecção direta ou a partir de blocos de CAD/CAM, na qual a sua polimerização é feita sob condições de pressão e temperatura elevadas, o que leva a uma taxa de conversão superior e à limitação da contração de polimerização. Foram utilizadas as bases de dados do MEDLINE, via PubMed, ResearchGate, e ScienceDirect, para pesquisa de artigos de investigação, revisões bibliográficas e casos clínicos. Foi ainda utilizado um livro. Esta revisão bibliográfica aborda o papel das restaurações indiretas posteriores em resina composta e a importância dos diferentes passos da técnica, desde os princípios da preparação da cavidade, impressão, provisionalização e cimentação da peça, abordando conceitos como cavity design optimization (CDO), immediate dentin sealing (IDS) e deep margin elevation (DME), referindo os materiais mais utilizados e a importância que os mesmos têm para o sucesso da restauração. É abordada a longevidade das restaurações indiretas em resina composta, sendo que a taxa anual de insucesso é de 1,6% a 4,8%. A longevidade das restaurações dependente de vários fatores relacionados com o material, paciente e clínico. Apesar das restaurações indiretas em resina composta demonstrarem uma elevada taxa de sucesso, na ordem dos 90%, para a restauração de grandes destruições dentárias, existe ainda uma necessidade de investigação a longo prazo que relacione a longevidade e sucesso das restaurações indiretas em resina composta com outros materiais, no sentido de se poder tirar conclusões relativamente a este tema.

Composite resin indirect restorations were introduced with a view to overcoming the limitations of the direct technique’s composite resins, which, despite its evolution in terms of constitution and proprieties, still presented limitations concerning mechanical proprieties and polymerization shrinkage. The indirect technique allows manufacture of composite resin in an extra-oral environment, in the laboratory by waxing, directly made or from the sintering of CAD/CAM blocks, in which the polymerization is carried out under high pressure and temperature conditions, which leads to a higher conversion rate and a limitation of the polymerization shrinkage. MEDLINE, Pubmed, ResearchGate and ScienceDirect databases were used, for the selection of research articles, literature reviews and case reports. Also, a book was consulted. This literature review approaches the role of posterior indirect restorations in composite resin and the importance of the different…

Advisors/Committee Members: Carracho, José Fausto 1975-.

▼ 

Tese de mestrado, Medicina Dentária, Universidade de Lisboa, Faculdade de Medicina Dentária, 2016

Objetivos: Esclarecer de que forma a utilização de glicerina afeta a microdureza de resinas compostas, e se esta permite prevenir a formação da camada superficial de resina composta inibida pelo O2. Materiais e Métodos: Fotopolimerizaram-se discos de compósito com LED, durante 20 segundos, através de matrizes oclusais de polivinilsiloxano [Registrado Clear (VOCO) e Memosil®2 (Heraeus Kulzer)], de acetato e sem matrizes. Ainda se recorreu a diferentes protocolos de aplicação de glicerina previamente à fotopolimerização. Os grupos foram divididos por dois estudos (n=10). No estudo 1, avaliou-se o efeito da glicerina na microdureza do compósito. No estudo 2, avaliou-se a influência de três matrizes oclusais e de três protocolos de aplicação de glicerina na microdureza do compósito. Os testes de microdureza foram feitos 24 horas após a polimerização. Os resultados foram analisados com T-tests (p=0,05). Resultados: No estudo 1, a microdureza no topo do grupo fotopolimerizado com glicerina foi superior à do grupo fotopolimerizado sem glicerina (p<0,05), enquanto na base se verificou o contrário (p<0,05). No estudo 2, não houve diferenças na microdureza dos grupos fotopolimerizados com matriz de acetato (p>0,05). Entre os grupos fotopolimerizados com polivinilsiloxanos, aqueles que apresentaram maior microdureza de topo foram os fabricados com aplicação de glicerina na face interna da matriz (p<0,05); na microdureza da base apenas houve diferenças entre o grupo fotopolimerizado com Memosil®2 e os grupos que utilizaram Registrado Clear com glicerina (p<0,05). Conclusões: A glicerina promove o aumento da microdureza no topo da resina composta; quando aplicada na face interna das matrizes oclusais de PVS aumenta a microdureza superficial do compósito apesar de não apresentar vantagens quando aplicada na face externa das matrizes oclusais. A aplicação de glicerina juntamente com o Registrado Clear pode levar a uma diminuição da microdureza da base dos espécimes.

Objectives: Clarify how the use of glycerin affects the hardness of composite resins, and if this helps to prevent the formation of the composite resin surface layer inhibited by O2. Materials and Methods: Light curing to composite discs with a LED during 20 seconds, by polyvinylsiloxane occlusal matrix [Registrado Clear (VOCO) and Memosil®2 (Heraeus Kulzer)], and no acetate matrix. Different glycerin application protocols were used prior to curing. The groups were divided in two studies (n=10). On study 1, the effect of glycerin in the composite microhardness was evaluated. On study 2, the influence of three occlusal matrices and three glycerin application protocols in the composite microhardness was evaluated. The microhardness tests were performed 24 hours after curing. Results were analyzed using T-tests (p=0,05). Results: In study 1, the microhardness at the top of light-cured group with glycerin was superior to light-cured group without glycerine (p<0.05), while…

Advisors/Committee Members: Oliveira, Sofia Arantes e, 1973-.

▼ 

O objetivo deste estudo clínico controlado, aleatorizado e duplo-cego, foi comparar o desempenho clínico de uma resina à base de silorano com uma resina à base de metacrilato, em restaurações Classe II, compostas e complexas, ao longo de 18 meses. Após obtenção do consentimento livre e esclarecido, 33 participantes receberam 100 restaurações (n=50), alocadas aleatoriamente em grupo teste (Resina Filtek P90® e Sistema Adesivo Silorano 3M ESPE) ou grupo controle (Resina Filtek P60® e Adesivo Adper SE Plus® 3M ESPE). Após uma semana, as restaurações receberam acabamento e polimento. Um único operador realizou todos os procedimentos restauradores. Dois examinadores calibrados (kappa ponderado 0,7) avaliaram as restaurações no baseline e após 18 meses, de acordo com os critérios United States Public Health Service (USPHS) modificados. Os parâmetros analisados foram descoloração marginal, integridade marginal, textura de superficíe, forma anatômica, sensibilidade pós-operatória, cárie secundária, contato proximal e aspecto radiográfico. Os dados foram analisados com os testes Mann Whitney, Wilcoxon signed Rank, estatística Kaplan-Meier e análise de regressão de Cox (=0,05). Após 18 meses, 90% das restaurações foram avaliadas. Não houve diferença significativa entre os materiais no baseline ou após 18 meses (p>0,05). A análise de cada material ao longo do tempo demonstrou diferença significativa no grupo controle para descoloração marginal (p=0,046) e textura de superfície (p=0,005). Para o grupo teste houve diferença significativa para descoloração marginal (p=0,025), integridade marginal (p=0,046) e textura de superfície (p=0,005). Não houve diferença significativa entre as taxas de sobrevida observadas para os grupos teste (92%) e controle (98%) (p=0,185). Não houve efeito significativo do sistema restaurador (p=0,246), do tipo de dente (p=0,673) ou do número de faces restauradas (p=0,402) sobre as curvas de sobrevida. O desempenho clínico da resina de silorano foi similar ao da resina de metacrilato. As restaurações perderam em qualidade nos critérios descoloração marginal, integridade marginal e textura de superfície, mas continuaram aceitáveis após 18 meses. O sistema de resina à base de silorano é aceitável para restaurações Classe II.

The aim of this randomized, double-blind, controlled study was to compare the clinical performance of a silorane-based resin composite with a methacrylate-based resin composite in Class II restorations after 18-month follow-up. After obtaining informed consent, 33 patients received 100 direct Class II composite resin restorations (n=50) that were randomly allocated into a test group (Filtek P90R /Adhesive System - 3M ESPE) or control group (Filtek P60R /Adper SE PlusR - 3M ESPE). After one week, the restorations were finished and polished. A single operator performed all the restorative procedures. Two calibrated examiners (weight kappa . 0.7) assessed the restorations at the baseline and after 18 months, according to modified United States Public Health System (USPHS) criteria. The…

Advisors/Committee Members: Claudia Silami de Magalhaes, Allyson Nogueira Moreira, Claudia Silami de Magalhaes, Allyson Nogueira Moreira, Sergio Lima Santiago, Cecilia Pedroso Turssi, Tulimar Pereira Machado Cornacchia, Mauro Henrique Nogueira Guimaraes de Abreu.

▼ 

Estudou-se, in vitro, a influência dos sistemas adesivos e dos tempos para acabamento e polimento sobre a microinfiltração marginal em restaurações do tipo Cl V. Foram utilizados 150 caninos e pré-molares humanos (superiores e inferiores), hígidos, sem trincas ou fraturas de esmalte, armazenados em solução salina de Timol (0,9%), mantidos em refrigeração. Esses foram divididos, de forma aleatória, em três grupos com 50 elementos cada um, em função dos sistemas adesivos testados (Single Bond®, Etch &Prime®, SBMP®), e em cinco subgrupos: imediato; 24horas; 14 dias; 21 dias e 30 dias, com 10 dentes cada um, em função do tempo decorrido entre a confecção das restaurações e o acabamento e polimento. Os preparos cavitários apresentaram ângulo cavo superficial totalmente em esmalte, e as seguintes dimensões: mésio/distal- 4,0mm; ocluso/cervical-3,0mm e profundidade de 2,0mm, confeccionados com ponta diamantada, em alta velocidade, sob refrigeração água/ar. Até que fossem restaurados os dentes, foram armazenados em água destilada a 4ºC. Para os preparos cavitários que foram tratados com os sistemas adesivos Single Bond® e SBMP®, usou-se a resina Z-100®, enquanto a Degufill® foi utilizada para o sistema Etch &Prime®. Utilizou-se a técnica de inserção em três incrementos diagonais, sendo que cada um foi fotoativado duas vezes (40 segundos cada um). A primeira ativação utilizou um dispositivo distanciador com a intenção de reduzir a intensidade luminosa inicial (em torno de 50%). Os dentes foram selados, termociclados (500ciclos), imersos em fuccina básica a 0,5% por 24 horas, lavados, embutidos em resina de poliéster, seccionados e avaliados quanto à microinfiltração em estereomicroscópio com 25X de aumento, segundo um escore. Os resultados foram submetidos à análise estatística, para métodos não paramétricos (teste de Kruskal-Wallis), com nível de significância inferior a 5% (p<0,05). Algumas amostras foram analisadas em microscopia eletrônica de varredura (MEV). Foi verificado um grande número de fraturas de esmalte para os preparos restaurados com a resina Z-100®, em todos os períodos avaliados. Após a análise dos resultados, pode-se concluir, nas condições testadas neste experimento, que: 1º) nenhum sistema adesivo conseguiu impedir, de forma efetiva, a penetração do corante, em nenhum dos períodos analisados; 2º) o processo de sorpção de fluidos pelas resinas compostas diminuiu os valores para microinfiltração, com o passar do tempo; 3º) o sistema adesivo Etch &Prime® aparentou menor resistência de união às estruturas dentais do que os sistemas SBMP® e Single Bond®, que se mostraram mais eficientes neste quesito.

An in vitro study was performed in order to verify the influence of different adhesive systems and finishing and polishing times in relation to marginal micro-leakage in Blacks Class V restorations. A total of 150 human canines and premolars were used, and these were higid, with no enamel fractures, and kept in Timols saline solution (0.9%) at 4°C until used. The teeth were randomly divided into three groups…

Advisors/Committee Members: Luiz Thadeu de Abreu Poletto, Geraldo de Avila Junior, Lincoln Dias Lanza, Lincoln Dias Lanza.

▼ 

As resinas compostas fotoativáveis apresentam limitações inerentes ao sistema restaurador, como a tensão gerada durante a contração volumétrica de polimerização e a baixa resistência ao desgaste, principalmente nas regiões de contato oclusal. Na tentativa de diminuir estas tensões ou minimizar os seus efeitos, o uso de baixa densidade de potência nos momentos iniciais da reação de polimerização tem sido proposto. Acredita-se, no entanto, que as propriedades físicoquímicas do material possam ser afetadas negativamente, podendo resultar em um polímero mais frágil mecanicamente e mais susceptível à degradação. Face à esta problematização, avaliou-se o efeito que diferentes métodos de fotoativação exercem na resistência ao desgaste de uma resina composta, bem como na suscetibilidade da estrutura polimérica final formada, em função da variação do meio de armazenamento, aquoso ou alcoólico. O aparelho VIP (BISCO), que possibilita comandos independentes de densidade de potência e tempo foi selecionado. Quatro diferentes métodos de fotoativação foram investigados: Convencional (C: 600mW/cm2 X 40s), Pulse-delay (PD: 200mW/cm2 X 3s + 3 min + 600mW/cm2 X 37s), Pulse-delay plus (PDP: 600mW/cm2 X 3s + 3 min + 600mW/cm2 X 37s) e Softstart (SS: 200mW/cm2 X 10s + 600mW/cm2 X 30s). Após a fotoativação, os espécimes foram armazenados em dois meios distintos, água destilada e solução de etanol a 75%, por 24 horas, e submetidos ao teste de escovação simulada. Os dados foram analisados pelos testes estatísticos ANOVA à 2 critérios e key. Os métodos de fotoativação que utilizaram baixa densidade de potência inicial não comprometeram a resistência à abrasão da resina composta testada.

In an attempt to reduce the stresses generated during polymerization shrinkage of composite resins or minimize its effects, different light-curing techniques have been proposed as alternatives to the conventional technique, which are known as lightcuring modulation techniques, and suggest the use of low power density at the initial moments of the polymerization reaction. However, due to the low power density applied to the composite resin, it is believed that some properties of the material would be negatively affected, which might produce a polymer mechanically more fragile. Considering that, this study was conducted to investigate the in vitro abrasive wear of a composite resin subjected at four different photoactivation methods, as well as in the susceptibility of the final polymer structure formed, in function of the variation of the way of storage, watery or alcoholic. Device VIP (BISCO), that it makes possible independent commands of power density and time was selected. Four different photoactivation methods had been investigated: Conventional (C: 600mW/cm2 X 40s), Pulse-delay (PD: 200mW/cm2 X 3s 3 min wait 600mW/cm2 X 37s), Pulse-delay plus (PDP: 600mW/cm2 X 3s 3 min wait 600mW/cm2 X 37s) and Soft-start (SS: 200mW/cm2 X 10s 600mW/cm2 X 30s). After the photoactivation, the specimens had been stored in two distinct ways, distilled water and solution…

Advisors/Committee Members: Franco, Eduardo Batista.

▼ Abstract: The aim of this in vivo study was to evaluate clinically through the USPHS criteria and postoperative sensitivity in Class I restorations restored with etch-and-rinse and self-etch adhesive system. Thirty-two Class I amalgam restorations are replaced with adhesive restorations. After the cavity preparation, the restorations were made randomly, under rubber dam, using the following groups (n = 8): G1 - 2 Single Bond + Filtek Supreme XT (XT); G2 - Adper Easy Bond + XT; G3 - Adper Scotchbond + XT; G4 - Clearfil SE Bond + XT. Postoperative sensitivity was analyzed using scores before (T1) (baseline), after 15 days (T2), 12 months (T3) and 24 months (T4), using cold stimulus and analog pain scale. The clinical evaluation of restorations were performed by USPHS criteria. The clinical evaluation (color stability, marginal integrity, marginal change color, anatomic form and secondary caries) were performed at the times T2 and T4, by a single evaluator. At the end of the assessment, data were grouped and analyzed statistically. No statistically significant difference when we compared the postoperative sensitivity between groups during the analyzed times and all groups behaved similarly when we evaluated a single group during the time, presenting statistical difference in T2 if we compared to others . The USPHS modified criteria indicated that G2 (EB+XT) had a worse clinical performance with significant amounts of exchanged restorations (37.5% requiring replacement - Charlie scores) with modification of marginal adaptation and marginal staining, . The other groups behaved similarly. The restorations were considered acceptable after 24 months. It is concluded that the one-step self-etching adhesive system showed a lower restoration longevity if compared to other systems used. The 2-step self-etch, 2-step and 3-step etch-and-rinse adhesive systems showed similar clinical results Advisors/Committee Members: UNIVERSIDADE ESTADUAL DE CAMPINAS (CRUESP), Martins, Luís Roberto Marcondes, 1960- (advisor), Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba (institution), Programa de Pós-Graduação em Clínica Odontológica (nameofprogram), Braga, Roberto Ruggiero (committee member), Silva, Gisele Rodrigues da (committee member), Marchi, Giselle Maria (committee member), Lima, Débora Alves Nunes Leite (committee member).

▼ 

O propósito deste trabalho foi estudar o efeito de métodos de contensão da mufla metálica (grampo convencional e sistema RS de contensão) e do tempo pós-prensagem (imediato e 6 horas) nos níveis de adaptação da base de prótese total superior confeccionada com as resinas acrílicas ativadas termicamente Clássico (Clássico) e QC-20 (Dentsply). Foram confeccionados 80 conjuntos modelo de gesso-base de cera distribuídos aleatoriamente em 8 grupos (n=10), de acordo com os métodos de contensão de mufla metálica e do tempo pós-prensagem. As resinas acrílicas foram proporcionadas e manipuladas de acordo com as instruções dos fabricantes e prensadas na fase plástica, com carga inicial de 850 kgf e final de 1250 kgf em prensa hidráulica de bancada. As bases confeccionadas em resina Clássico foram polimerizadas em ciclo de água a 74?C por 9 horas e as bases de resina QC-20 em água em ebulição por 20 minutos. Depois de esfriadas até atingir a temperatura ambiente, as bases foram desincluídas, acabadas, fixadas nos respectivos modelos de gesso com adesivo à base de cianoacrilato e seccionadas em três secções, correspondentes à distal de caninos, mesial de primeiros molares e região palatina posterior. Em cada secção, o desajuste entre modelo de gesso e base de resina foi verificado nos pontos referenciais fundo de sulco vestibular direito e esquerdo, crista do rebordo alveolar direito e esquerdo e linha mediana palatina posterior, com microscópio comparador linear Olympus, com precisão de 0,0005 mm. Os resultados coletados foram submetidos à análise de variância e ao teste de Tukey (5%). O dispositivo RS produziu níveis médios de adaptação com diferença estatística significante quando comparado com o grampo convencional, independente dos demais fatores. O dispositivo RS produziu níveis médios de adaptação nos tempos imediato e 6 horas com diferença estatística significante quando comparado com o grampo convencional. A polimerização imediata produziu valores entre cortes sem diferença estatística significativa quando comparada com a polimerização após 6 horas. Quando os cortes foram analisados no fator prensagem, os melhores níveis de adaptação foram obtidos com o dispositivo RS, com diferença estatística significativa quando comparado com o grampo convencional. Os tratamentos RS e convencional apresentaram comportamento semelhante, independente da resina, mas foram diferentes no tempo pós-prensagem. A região posterior apresentou maiores valores de desadaptação em ambas as resinas, independente do tipo de contensão da mufla e do tempo pós-prensagem

The purpose of this study was to verify the effect of flask closure method (conventional clamp and RS tension system) and post-pressing time (immediate and after 6 hours) on the maxillary denture base adaptation made with Classico and QC-20 heat?cured acrylic resins. Eighty maxillary stone cast/wax base sets were made and randomly assigned into 8 groups (n=10) according to the flask closure method and post- pressing time. The acrylic resins were proportioned and manipulated following…

Advisors/Committee Members: Tarcisio Jose de Arruda Paes Junior, Rafael Leonardo Xediek Consani, Marcelo Ferraz Mesquita, Rafael Leonardo Xediek Consani [Orientador].

▼ 

Dissertação para obtenção do grau de Mestre no Instituto Superior de Ciências da Saúde Egas Moniz

Objetivos: Avaliar a rugosidade de superfície e a cor de resinas compostas após a exposição a agentes branqueadores com recurso a microscopia eletrónica de varrimento (SEM) e espectrofotometria de reflexão. Materiais e Métodos: Sessenta discos de compósito (10 mm de diâmetro e 2 mm de espessura) foram confecionados a partir de três resinas compostas fotopolimerizáveis (Filtek Supreme XTE, Filtek Z250 e Enamel plus Hri). Cada resina composta possuía um grupo de controlo (n=5), um grupo submetido a branqueamento com peróxido de hidrogénio 6% durante 8 horas diárias (n=5), um grupo submetido a branqueamento com peróxido de hidrogénio 6% durante 30 minutos, duas vezes por dia (n=5) e outro grupo submetido a peróxido de carbamida 10% durante 8 horas diárias (n=5). O contacto com a solução branqueadora foi realizado durante 21 dias, tendo sido testado ao 1ºdia, ao 14ºdia e ao 21ºdia. Todas as amostras foram analisadas através de SEM e Spectroshade Micro, de forma a serem detetadas alterações na rugosidade de superfície e cor das mesmas. Resultados: A análise das micrografias do SEM de ambos os compósitos expostos a PC 10% e PH 6% mostrou alterações na rugosidade de superfície, nomeadamente fendas superficiais e numerosos poros, destacando uma real separação entre a matriz orgânica e as partículas de carga inorgânica, independentemente da concentração do gel. Estas alterações foram mais pronunciadas no compósito nanoparticulado e nanohíbrido, Filtek Supreme XTE e Enamel Hri Plus respetivamente. Além disso, não foram detetadas diferenças significativas de cor (ΔE) entre os materiais testados (p>0,05). Conclusões: Com base nos resultados deste estudo, concluiu-se que o peróxido de carbamida 10% e o peróxido de hidrogénio 6% não induzem alterações de cor clinicamente significantes às resinas compostas testadas (ΔE<3,3), apesar do aumento na rugosidade de superfície.

Advisors/Committee Members: Pinto, Alexandra, Fernandes, Inês Caldeira.

▼ 

Dissertação para obtenção do grau de Mestre no Instituto Superior de Ciências da Saúde Egas Moniz

Objetivo: O objetivo deste trabalho foi quantificar a alteração de cor e de degradação de superfície de duas resinas compostas, utilizadas em restaurações diretas na Medicina Dentária atual, após serem imersas em diferentes colutórios. Materiais e Métodos: Foram confecionadas 60 amostras, com 10mm de diâmetro por 2 mm de altura, de cada resina composta: uma nanoparticulada Filtek™ Supreme XTE (3M ESPE – Minnesota, USA) e outra microhíbrida Filtek™ Z250 (3M ESPE – Minnesota, USA). As amostras foram subdivididas em grupos e sujeitas a uma imersão diária com agitação no Vórtex, cinco vezes por semana durante 3 semanas em diferentes soluções: água destilada (Grupo de controlo), Bexident, Hextril Menta, Listerine Dentes&Gengivas, Oral – B Complete e Perio-aid. No período entre as imersões as amostras foram armazenadas em água destilada numa estufa a 37ºC. Após as imersões, as amostras foram analisadas com Espetrofotómetro. A alteração de cor foi calculada através dos sistema CIE L* a* b*. Posteriormente, selecionaram-se 3 amostras aleatórias de cada grupo para analisar a degradação da superfície com Scanning Electron Microscope (SEM). Os resultados obtidos pela análise com espetrofotómetro foram tratados estatisticamente pelo software SPSS, através de estatística descritiva e comparativa (Teste ANOVA One-way e t de Student), com nível de significância de 5%. Resultados: A imersão das resinas compostas nos diferentes colutórios provocou degradação superficial e alteração de cor mais evidentes na Resina Composta Filtek™ Supreme XTE. O colutório Hextril foi o responsável pela maior degradação superficial em ambas as Resinas Compostas, enquanto o colutório Oral-B demonstrou causar variações de cor significativas na Resina Filtek ™ Supreme XTE. Conclusões: As resinas compostas sofrem alterações de morfologia e de cor quando expostas à ação de diferentes colutórios. A intensidade das alterações varia consoante a composição das Resinas Compostas e das soluções de bochecho.

Advisors/Committee Members: Amorim, Armanda.

▼ 

Dissertação para obtenção do grau de Mestre no Instituto Superior de Ciências da Saúde Egas Moniz

As resinas compostas são biomateriais, normalmente utilizadas na prática clínica nomeadamente em Medicina Dentária, com o objectivo de reabilitar a estrutura dentária perdida devido a cáries, processos erosivos e fracturas, bem como a função e a estética. Idealmente, os materiais dentários não deveriam produzir efeitos adversos nos tecidos orais, nomeadamente as resinas compostas amplamente utilizadas pelos profissionais de saúde oral, no entanto, estas libertam substâncias que podem comprometer a sua biocompatibilidade. Os monómeros residuais que são libertados deste tipo de materiais são o resultado do grau de polimerização incompleto ou de processos de degradação e de erosão. O objectivo desta monografia foi identificar quais os principais métodos utilizados para a avaliação do potencial citotóxico dos materiais utilizados correntemente, como as resinas compostas, os mecanismos celulares afectados de modo a sensibilizar o Médico Dentista sobre os eventuais riscos. Actualmente existe uma grande variedade de testes biológicos: in vitro e in vivo. Estes permitem a avaliação da resposta biológica dos tecidos aos materiais dentários. Os constituintes das resinas compostas, nomeadamente os monómeros podem ser libertados desencadeando nas células efeitos citotóxicos e genotóxicos comprometendo assim as funções básicas das células. Todos os monómeros apresentam citotoxicidade, que se traduz essencialmente na diminuição dos níveis intracelulares de glutationa e no aumento de espécies reactivas de oxigénio provocando deste modo morte celular. Esta resulta maioritariamente em apoptose das células expostas a este tipo de materiais. O efeito genotóxico resulta da acção dos monómeros nas células provocando danos no DNA. Além disso, podem provocar inflamação nos tecidos adjacentes a estes materiais, inibir as funções celulares dos odontoblastos e consequentemente conduzir a atrasos nos processos de mineralização. A comparação dos efeitos dos vários monómeros caracterizados neste trabalho indica que o Bis-GMA é o mais citotóxico.

Advisors/Committee Members: Barahona, Isabel.

▼ Objectives: To evaluate depth of polimerization (DP), contraction strress (SC), flexural strenght (FS), elastic modulus (EM) and bond strength (BS) of three low-viscosity Bulk Fill composites resin compare as of high-viscosity traditional composites. Methods: Three Bulk fill composites (Filtek BKF, Surefil SDR, X-tra Base) and three traditional ( Z250 XT, Grandioso, TPH3) were used. For FS/ME, 60 (n=10) bar specimens (7 mm x 2 mm x 1 mm) were prepared and evaluated with Universal Testing Machine (UTM). For DP e BS, conical cavities (n=10) were prepared in bovine dentine and restored with materials. DP was analyzed trough the ratio base/top with microhardness of surface and BS on the push-out test in UTM. SC was measured for to increment one of Bulk Fill Resins and two increments of traditional resins in UTM attached to a extensometer (n=5). The data were statistically evaluated by ANOVA 2-way/Tukey (p<0,05). Results: For EM the conventional resins show higher values compare to all the BKF resins, however for the FS they were the same, except for only the VOCO Bulk Fill that was inferior. For the PP, conventional and BKF were statistically similar. In TC and in BS the BKF were superior to conventional, also with the exception of Xtra Base Bulk Fill (VOCO), which was statistically the same as the conventional ones in the BS. Conclusion: The Bulk Fill composites resin BKF and SDR present most of property physical and mechanical higher or similar than traditional composites, except the elastic modulus. Advisors/Committee Members: Borges, Boniek Castillo Dutra (advisor), 06140107482 (advisor).

▼ O objetivo do presente estudo in vitro, foi de avaliar a dureza Knoop das resinas compostas Charisma (C) e Durafill VS (D) quando polimerizadas: na temperatura do ambiente (A) (23+-1C); refrigerada (4+-1C), com tempo de espera de 15 minutos após a remoção do refrigerador para fotoativação, (15). Cento e vinte corpos-de-prova com 4 mm de diâmetro por 2 mm de altura foram confeccionados em uma matriz de aço inoxidável. O material resinoso foi manualmente inserido na matriz com o auxílio de uma espátula e fotoativado por 20 segundos, como recomendado pelo fabricante. Cada corpo-de-prova foi testado imediatamente após a fotoativação (I) e, após sete dias de armazenamento (7d) em ambiente escuro com umidade relativa a 100%, à temperatura do ambiente (23+-1C). Os valores obtidos foram submetidos à análise de variância e ao teste de Tukey HSD (5%). Os resultados mostraram que a resina composta C apresentou maiores valores estatísticos de dureza que a D, e, quando testada imediatamente após a polimerização apresentou dureza maior em Cai estatisticamente semelhante à C15i, na superfície do topo. Já na base, a resina composta Cai, teve maiores valores de dureza quando comparados à Coi e C15i. Os grupos do material D não mostraram diferenças significantes com relação ao efeito da refrigeração nem no topo nem na base. Sete dias após, os valores de dureza Knoop caíram tanto para C7d, quanto para D7d e não diferiram entre as situações de temperatura ambiente e de tempo da remoção do refrigerador. Advisors/Committee Members: Janaína Bertoncelo de Almeida.

▼ 

Tese de mestrado, Medicina Dentária, Universidade de Lisboa, Faculdade de Medicina Dentária, 2016

A fluorescência é uma propriedade ótica das estruturas dentárias observada quando a radiação ultravioleta (UV) incide sobre os dentes, fazendo com que estes apareçam brancos e brilhantes à luz do dia. As resinas compostas (RC) utilizadas em restaurações anteriores, devem mimetizar estas características dos dentes de forma a se obter um excelente resultado final estético, que satisfaça o médico dentista e o paciente. O presente estudo tem como objetivo avaliar, in vitro, a fluorescência de vários tipos de RCs utilizadas em restaurações diretas de dentes anteriores (“Esmalte artifici-al”, “Dentina artificial” e “Incisal”), comparando-a a dentes anteriores humanos (esmalte e dentina). Foi ainda avaliado se o aumento de croma das RC, dentro do mesmo sistema, tem influência nesta característica ótica. Realizaram-se 63 espécimes RCs, de diferentes fabricantes, com 10mm de diâmetro por 2mm de altura, e se preparou 4 dentes anteriores humanos, que posteriormente foram unicamente iluminados com radiação UV e obtidas imagens digitais individuais de cada um dos espécimes, tendo-se avaliado através do software (Adobe Photoshop CC versão 2015.0.0 da Adobe Systems, Inc) o valor de “b”, da banda azul de cada imagem, cujo valor está relacionado diretamente com o nível de fluorescência do espécime. A análise dos resultados permite verificar uma grande variação dos valores de “b”, desde 52 até 253, e que nenhum dos espécimes de RCs avaliados apresentou fluorescência igual ao “Esmalte Natural” e/ou “Dentina Natural” avaliados, contudo, existiram algumas RC que exibiram níveis fluorescência muitos semelhante às estruturas dentárias em estudo. Outras RCs apresentaram uma fluorescência consideravelmente inferior ao “Esmalte Natural” e outros espécimes com fluorescência ligeiramente superior à “Dentina Natural”. Em certos fabricantes, verificou-se que o aumento de croma das RCs, dentro do mesmo sistema, tem influência na sua emissão de fluorescência.

Fluorescence is an optical property of dental structures observed when ultraviolet (UV) radiation falls in to the teeth, causing them to appear bright and white during the daylight. The composite resins (RC) used in anterior restorations must mimic these characteristic of the teeth, in order to obtain an excellent final aesthetic result which satisfies the dentist and patient. This study aims to evaluate in vitro fluorescency of various types of RC used in direct restorations of anterior teeth ("Artificial Enamel", "Artificial Dentine," and "Incisal"), comparing them to human anterior teeth (enamel and dentin). It was also assessed whether the increased in the chroma of the RC, within the same system, has an influence on this optical characteristic. There were 63 RCs specimens, from different manufactures, 10mm in diameter and 2mm in height, and prepared 4 human anterior teeth, which were then only illuminated with UV radiation and obtained individual digital images of each of the specimens,…

Advisors/Committee Members: Cavalheiro, Alexandre, 1974-.

▼ 

Tese de mestrado, Medicina Dentária, Universidade de Lisboa, Faculdade de Medicina Dentária, 2016

Os avanços na Dentisteria levaram à demanda de restaurações estéticas posteriores com longa durabilidade. Os onlays em resina composta, caracterizados pelas suas boas propriedades estéticas e mecânicas e pela sua fácil reparação, surgiram como uma resposta a esta demanda. Atualmente são cimentados à estrutura dentária mediante a utilização de cimentos resinosos que permitem uma adesão micromecânica da restauração à dentina. A principal causa da falha das restaurações indiretas está relacionada com a deterioração da integridade marginal e da eficácia da adesão, consequente de uma selagem incompleta da interface entre o dente e a restauração. Desde a introdução do bisfenol-glicidilmetacrilato na Dentisteria que a composição das resinas compostas tem evoluído continuamente, melhorando as suas propriedades físicas e expandindo os seus campos de aplicação clínica. Estas são frequentemente caracterizadas consoante o seu mecanismo de ativação em auto-polimerizáveis, de dupla-polimerização e foto-polimerizáveis. De forma a melhorar as propriedades das resinas compostas, foi proposto o seu aquecimento em dispositivos próprios previamente à sua utilização. Desta forma, resinas compostas com maior teor de partículas de carga, e, consequentemente, maior viscosidade, poder-se-iam tornar mais fluídas, facilitando a sua adaptação e penetração na dentina, e manter as suas boas propriedades mecânicas. Além disso, o aquecimento das resinas iria ter influência na polimerização, na medida em que a mobilidade dos radicais livres seria aumentada, levando a um maior grau de polimerização e, consequentemente, melhores propriedades mecânicas dos polímeros. Desta forma é importante estudar os efeitos do aquecimento de resinas compostas para posteriormente serem utilizadas como agente de cimentação de restaurações indiretas. Existem, no entanto, poucos estudos sobre o assunto em questão e a maioria debruça-se sobre as resinas de dupla polimerização, onde as desvantagens parecem superar as vantagens devido à drástica redução do seu tempo de trabalho que as torna, muitas vezes, inutilizáveis.

The advances on Dentistry resulted on the demand of esthetical posterior restorations with high durability. Composite onlays, characterized by their great esthetical and mechanical properties and their ease of repair, appeared as a response to this demand. Currently these are luted to the tooth with resin cements, which allows a micromechanical bond of the restoration to the dentin. The main reason for an indirect restoration failure is related to the deterioration of the marginal integrity and bond efficiency as result of an incomplete interface sealing between the tooth and the restoration. Since the introduction of Bisphenol-glycidyl methacrylate on Dentistry, resin composite formulations have been continuously evolving, improving their physical properties and expanding their clinical applications. These are frequently characterized by their means of…

Advisors/Committee Members: Pequeno, Ana.

▼ O objetivo deste estudo foi avaliar e comparar as propriedades mecânicas selecionadas (resistência à tração diametral, microdureza Knoop) e conteúdo de carga em peso pela análise termogravimétrica (TGA) de cinco marcas comerciais de resina composta diferentes em matriz orgânica e carga nas cores A2 esmalte e dentina: 4Seasons (4S), Ivoclar Vivadent; Esthet-X improved (EX), Dentsply; Filtek Supreme (SU), 3MESPE; Grandio (GR), Voco e Palfique Estelite (PE), Tokuyama Dental Corp. Para cada grupo, a resistência à tração diametral (n=10), a microdureza Knoop (n=10) e o conteúdo de carga em peso pela análise termogravimétrica foram determinados. Os resultados obtidos nos ensaios foram comparados estatisticamente com análise de variância e Tukey (J = 0,05). As médias obtidas para resistência à tração diametral (MPa) foram: 4S dentina 36,08 b e 4S esmalte 39,26 ab ; EX dentina 44,44 ab e EX esmalte 45,12 ab ; GR dentina 45,23 ab e GR esmalte 49,24 a ; SU dentina 46,86 ab e SU esmalte 48,25 ab ; PE dentina 38,69 ab ; PE esmalte 38,58 ab (p < 0,05). As médias obtidas para microdureza Knoop (KHN) foram: 4S dentina 61,6b e 4S esmalte 57,98b; EX dentina 73,6b e EX esmalte 54,45b; GR dentina 123,90a e GR esmalte 74,89b ; SU dentina 101,30a e SU esmalte 123,10a ; PE dentina 55,89b ; PE esmalte 61,70b (p < 0,05). Para o conteúdo de carga em peso (wt%): 4S dentina 75,84 e 4S esmalte 76,37; EX dentina 76,80 e EX esmalte 75,75 ; GR dentina 86,89 e GR esmalte 87,00 ; SU dentina 76,22 e SU esmalte 76,54 ; PE dentina 71,62; PE esmalte 70,56. Os compósitos testados não apresentaram comportamento mecânico similar quanto à resistência à tração diametral e microdureza Knoop. Não foi observada diferença quando as pastas esmalte e dentina foram comparadas com exceção da resina Grandio no teste de microdureza. A maior resistência à tração diametral foi observada para a Grandio esmalte enquanto a 4 Seasons dentina apresentou a mais baixa média (p < 0,05). No teste de microdureza Knoop, a resina Filtek Supreme em ambas as pastas e a Grandio dentina apresentaram as maiores médias em comparação aos demais grupos (p < 0,05). Advisors/Committee Members: Eduardo Gonçalves Mota.

▼ O objetivo deste estudo foi avaliar o valamento marginal em restaurações de resina composta após ensaio de abrasão por escovação. Para isto, foram realizadas quatro restaurações na face vestibular de 12 incisivos bovinos, devidamente planificados e incluídos em resina acrílica. Os compósitos avaliados foram: Filtek Supreme XT, Filtek Z350 (3M/ESPE), ambos com nanopartículas, 4Seasons e Tetric Ceram HB (Ivoclar Vivadent), classificados como híbridos. Cada uma das 12 amostras foi submetida ao ensaio de abrasão em máquina de escovação (Idéia-PUCRS), com escova (Colgate Professional, Colgate-Palmolive) e dentifrício (Colgate Tripla Ação, Colgate-Palmolive), nos períodos correspondentes a 1, 2, 4 e 6 anos de escovação simulada. Para a análise do valamento marginal, antes e após cada período, foi utilizado um Perfilômetro XP-2 (Ambios Technology), sendo realizadas 5 varreduras em cada uma das restaurações das 12 amostras, após cada período. A média destas 5 varreduras foi calculada utilizando o software Origin 7.0 (OriginLab Corporation) gerando um gráfico (n=240) onde foi possível medir a discrepância entre a margem em esmalte e a resina composta, nos dois lados da restauração. A média dos dois lados foi tomada como sendo o valor de valamento marginal, em μm, da resina no período avaliado. Os resultados foram submetidos à Análise de Variância por Modelos Mistos para Medidas Repetidas com Parcela Subdividida e para a análise pós-teste foi utilizado o ajuste de Tukey com nível de significância de 5%. Todas as resinas apresentaram um aumento no valamento marginal ao longo dos períodos avaliados. Tanto a resina 4Seasons como a Tetric Ceram HB apresentaram um aumento significativo no valamento marginal após 4 e 6 anos de escovação simulada e não apresentaram diferenças estatisticamente significativas entre si em cada período. A resina Filtek Supreme XT não apresentou aumento significativo ao longo dos períodos avaliados. A Filtek Z350 apresentou aumento significativo do valamento marginal no período de 6 anos, sem apresentar diferenças estatisticamente significantes nos períodos de 1, 2 e 4 anos. Os aspectos morfológicos, de amostras de cada resina observadas em MEV, após cada período avaliado, ilustram o comportamento dos compósitos ao longo do tempo frente ao ensaio de abrasão por escovação. As interfaces dente/restauração das restaurações realizadas com os compósitos Filtek Supreme XT e Filtek Z350 apresentaram menor formação de valamento marginal após a abrasão por escovação ao longo do tempo Advisors/Committee Members: Hugo Mitsuo Silva Oshima.

▼ 

O objetivo do presente trabalho foi avaliar a contração de polimerização de quatro resinas compostas: Filtek Z250 (3M/ESPE), Filtek Supreme (3M/ESPE), Admira (Voco), Grandio (Voco), polimerizadas por fonte de luz halógena convencional. A avaliação realizou-se utilizando três metodologias diferentes. A primeira obtida em uma máquina de ensaios. Foram confeccionadas duas bases idênticas de metal de forma retangular. Estas bases foram colocadas paralelas na máquina, uma delas conectada ao braço móvel da máquina de ensaios e a outra ao braço fixo. A resina composta foi introduzida dentro do espaço de 1mm entre as duas bases (fator de configuração 1.5). O programa de computador manteve a máquina imóvel, medindo as forças transmitidas pelo material durante a presa desde o início da ativação até 120 segundos, mesmo depois de terminada a fotoativação. A segunda metodologia avaliou a contração linear livre da resina em uma matriz de teflon com uma cavidade interna retangular com os ângulos arredondados medindo 12 mm de comprimento, 5 mm de largura e 2 mm de profundidade. A resina foi condensada nessa cavidade e fotoativada. Após a polimerização calculou-se a contração linear do corpo de prova. A terceira metodologia avaliou a contração parede a parede, em cavidade cilíndricas de dentina bovina, que mediram 3 mm de diâmetro e 1,5 mm de profundidade. Após a polimerização calculou-se a contração parede a parede, em função do diâmetro da cavidade e da medida de fendas marginais observadas. Os resultados mostraram na primeira metodologia as médias das forças de contração de polimerização das resinas compostas: Grandio - 12.18N + 0,428, Filtek Z250 - 11.80N ± 0,760, Filtek Supreme - 11.80N ± 0,707 e Admira 11.89N ± 0,647; na segunda metodologia (contração linear livre) as médias das porcentagens da contração linear foram: Filtek Z250 - 0,51% ± 0,0357, Filtek Supreme - 0,36% ± 0,0438, Admira - 0,25 % ± 0,0346 e Grandio - 0,16 % ± 0,008; na terceira metodologia (contração parede a parede), as médias das medidas das fendas marginais foram: Filtek Z250 - 11,33 µm ± 2,160; Filtek Supreme - 10,66 µm ± 1,211, Admira - 11,16 µm ± 2,041 e Grandio - 10,50 µm ± 1,224.

One of the main problems of resin composite is the shrinkage they present during polymerization. The aim of this study was to compare polymerization contraction of selected resin composites by three different methods. A conventional halogen lamp-curing unit was used. In the first part of the study, composites were inserted into 1 mm space between 2 rectangular parallel steel bases, which surfaces measured 6x2 mm. One of the steel bases was connected to a 20 kgf load cell of a universal testing machine (EMIC-DL-500, Brasil). The volume of each sample was 12 mm3. The composites were activated for 20 seconds and the polymerization contraction forces measured during 120 s after the beginning of activaction. The contraction forces were: Grandio - 12,18 ± 0,428N; Filtek Z 250 – 11,80 ± 0,760N; Filtek Supreme – 11,80 ± 0707 N and Admira – 11,89 ± 0647 N. In the second part of the…

Advisors/Committee Members: Araujo, Paulo Amarante de.

▼ 

As forças geradas durante a polimerização das resinas estão relacionadas a vários fatores, sendo de muita importância a avaliação das forças que podem alcançar a interface adesiva nestas restaurações. O objetivo deste trabalho foi determinar estas forças, em função da composição e modo de ativação da resina, fonte de luz utilizada na ativação, e presença de material intermediário. Foram utilizadas duas bases de aço em forma retangular (6 x 2 mm), posicionadas paralelamente, sendo uma conectada ao braço móvel da máquina de ensaios (Emic – DL 500), através de uma célula de carga de 10 Kgf, e outra ao braço fixo. As resinas compostas foram introduzidas entre as bases metálicas, com 1 mm de altura, volume de 12 mm3 e fator C 1,5. As bases ficaram fixas durante o ensaio, e as forças geradas durante a polimerização foram registradas através de uma curva força/tempo, num total de dez ensaios para cada grupo. Foi avaliada a resina quimicamente ativada Concise (3M), as fotoativadas de micropartículas Filtek A-110 (3M), microhíbrida Filtek Z-250 (3M) e de alta viscosidade Filtek P-60 (3M). Dentre os aparelhos fotoativadores, foi avaliado o halógeno Spectrum (Dentsply), e os LEDs Ultraled (Dabi-Atlante) e Ultrablue IS (DMC). Os materiais intermediários avaliados foram o cimento de íonômero de vidro modificado por resina Vitrebond (3M) e a resina de baixa viscosidade Filtek Flow (3M). Os resultados mostraram que a resina quimicamente ativada Concise apresentou a menor força de contração de polimerização (4,216 + 0,353N), sendo este valor significantemente menor àqueles apresentados pelas resinas compostas fotoativadas (p<0,05). A resina de micropartículas Filtek A-110 apresentou a maior média dentre as resinas fotoativadas (8,365 + 0,5956N), sem diferenças estatisticamente significativas com Filtek P-60 (8,111 + 0,6868N) (p>0,05) e com diferenças estatisticamente significativas em relação a Filtek Z-250 (7,500 + 0,6149N) (p<0,05). Dentre os aparelhos fotoativadores o grupo polimerizado com Ultraled apresentou media significantemente menor que os outros grupos avaliados (5,175 + 0,3480N) (p<0,05). O grupo polimerizado com Spectrum (6,316 + 0,2175N) não apresentou diferenças estatisticamente significativas em relação a Ultrablue IS (p>0,05). Os grupos fotoativados com Ultrablue IS, a densidades de potência de 300 e 600 mW/cm2 (6,108 + 0,2252N e 6,497 + 0,2565N respectivamente) mostraram diferenças estatisticamente significativas entre eles (p<0,05). Finalmente, os resultados mostraram que existiram diferenças estatisticamente significativas entre os valores de forças de contração que foram registrados para a resina composta Filtek Z-250 com e sem material intermediário (p<0,05), sendo esta diferença positiva para o Vitrebond e negativa para o Filtek Flow. Pode-se concluir que todas as variáveis estudadas influíram significativamente nas forças de contração de polimerização em maior ou menor grau.

The aim of this study was to verify the influence of the type of composite resin (chemical-cured and three different type of…

Advisors/Committee Members: Mondelli, Rafael Francisco Lia.