Title CORRELATING THERMAL PROPERTIES OF SPUTTERED TANTALUM AND TANTALUM NITRIDE THIN FILMS OF VARYING N2 CONTENT WITH MECHANICAL, ELECTRICAL AND STRUCTURAL PROPERTIES
URL
Publication Date
Date Accessioned
Degree M.S., Materials Science and Engineering
Discipline/Department Materials Science and Engineering
Degree Level masters
University/Publisher Cornell University
Abstract With rapid growth in the semiconductor industry, the need for optimization of nanofabrication processes is ever increasing. In such processes, TaN films are of great interest as they create effective diffusion barriers against Cu interconnects in integrated circuits. These circuits may be subjected to elevated temperatures during processing and it is important to study the changes in properties of materials involved. Surprisingly, limited data on the constant pressure specific heat capacity (cp) of Ta and TaN thin films exist. This thesis studies the changes in cp from room temperature to 400°C of sputter-deposited Ta and TaN thin films with varied N2 partial pressure. Parallel studies of mechanical, electrical and structural changes are conducted on as-deposited and annealed samples to correlate to changes in cp. The cp of films increases with temperature, as seen in bulk forms of Ta and TaN. Low temperature resistivity measurements are performed to study the effect of lattice vibrations decreasing. The electrical properties of TaN, deposited in greater than 23% N2 content, are found to be insulating. Annealing decreases the resistivity of Ta films which is attributed to defect healing. The hardness and Young’s modulus increase up to 27% N2 content of TaN films. The residual stress in these films range from highly tensile Ta to increasingly compressive TaN with increased N2 content. The TaN film with the lowest inducing stress was 18% N2 with a compressive stress of -5.82 MPa.
Subjects/Keywords Thermal; electrical; semiconductor; Nanoindentation; thin films; Materials Science; Nanotechnology; Engineering; tantalum nitride
Contributors Van Dover, Robert B. (chair); Ast, Dieter G. (committee member); Phoenix, Stuart Leigh (committee member)
Language en
Country of Publication us
Record ID handle:1813/56807
Repository cornell
Date Retrieved
Date Indexed 2020-09-09
Grantor Cornell University
Issued Date 2017-08-30 00:00:00

Sample Search Hits | Sample Images | Cited Works

…wonderful conversations where we shared our passion for baking. You are one of the loveliest people I have met so far. Finally, thank you Cornell University for accepting me. You are the reason I am where I am and will be in the future. I truly felt like I…

…x5D;. Nanoindentations were performed by Joseph Carloni, a PhD student in the Materials Science and Engineering department at Cornell University, who works with Professor Shefford Baker. A Hysitron “TriboIndenter” (TI-900) in Bard Hall…

Cornell University is used for these measurements. The nanoindenter probe used for measurements is a “Berkovich” shaped (see Figure 9 below) diamond probe with a ~120 nm radius at the tip. The shape of the tip is a three-sided pyramidal shape…

…Bruker D8 GADDS, available in Bard Hall at Cornell University, uses a poly-cap focusing system to focus a very intense beam from an X-ray source onto the sample. The beams can be aligned down to 0.3mm which reduces the requirement for sample size to…

.